| n |
F |
4Q11-23-11 |
2Q5-31-11 |
3Q8-24-11 |
ln(-ln(1-F)) |
|
|
|
|
|
|
|
|
|
|
| 1 |
0.039958402 |
7.9 |
15.6 |
15.7 |
-3.1996 |
|
| 2 |
0.079956802 |
13.8 |
15.6 |
16.1 |
-2.48489 |
|
| 3 |
0.119955202 |
15.4 |
15.6 |
16.4 |
-2.05743 |
|
| 4 |
0.159953602 |
15.5 |
15.6 |
16.7 |
-1.74699 |
|
| 5 |
0.199952002 |
15.5 |
15.6 |
16.9 |
-1.50021 |
|
| 6 |
0.239950402 |
15.5 |
15.6 |
17 |
-1.29327 |
|
| 7 |
0.279948802 |
15.5 |
15.7 |
17.1 |
-1.11342 |
|
| 8 |
0.319947202 |
15.6 |
15.7 |
17.2 |
-0.95299 |
|
| 9 |
0.359945602 |
15.6 |
15.7 |
17.2 |
-0.80698 |
|
| 10 |
0.399944002 |
15.6 |
15.7 |
17.2 |
-0.67191 |
|
| 11 |
0.439942402 |
15.6 |
15.7 |
17.3 |
-0.54522 |
|
| 12 |
0.479940802 |
15.6 |
15.7 |
17.3 |
-0.42493 |
|
| 13 |
0.519939202 |
15.6 |
15.7 |
17.3 |
-0.30946 |
|
| 14 |
0.559937602 |
15.6 |
15.7 |
17.4 |
-0.19743 |
|
| 15 |
0.599936003 |
15.6 |
15.7 |
17.4 |
-0.0876 |
|
| 16 |
0.639934403 |
15.6 |
15.7 |
17.4 |
0.021242 |
|
| 17 |
0.679932803 |
15.7 |
15.7 |
17.5 |
0.130348 |
|
| 18 |
0.719931203 |
15.7 |
15.7 |
17.6 |
0.241156 |
|
| 19 |
0.759929603 |
15.7 |
15.8 |
17.7 |
0.35545 |
|
| 20 |
0.799928003 |
15.8 |
15.8 |
17.8 |
0.475661 |
|
| 21 |
0.839926403 |
15.8 |
15.8 |
17.9 |
0.605475 |
|
| 22 |
0.879924803 |
15.9 |
15.8 |
18.1 |
0.751245 |
|
| 23 |
0.919923203 |
15.9 |
15.8 |
18.3 |
0.92615 |
|
| 24 |
0.959921603 |
16 |
15.8 |
18.5 |
1.168424 |
|
| 25 |
0.999920003 |
16 |
15.8 |
18.7 |
2.24427 |
|
|
Defect density |
800 |
0 |
0 |
/cm2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|